Title: | Assessment of glass-forming ability and the effect of La2O3 on crystallization mechanism of barium lead zinc phosphate glasses |
Authors: | Nascimento, Marcio Luis Ferreira Dantas, Noelio Oliveira |
metadata.dc.creator: | Nascimento, Marcio Luis Ferreira Dantas, Noelio Oliveira |
Abstract: | Differential scanning calorimetry (DSC) was used in this work to study the effect of La2O3 addition on crystallization mechanism of barium lead zinc phosphate glasses. Bulk glasses from two different routes (using P2O5 and H3PO4 as starting materials) presented only one crystallization peak. An assessment of glass-forming ability (GFA) was performed from recent theory that is connected to glass stability (GS), and is also correlated to critical cooling rate, qcr. Systems with high La2O3 content presented some of the highest GS values and estimated critical cooling rates (qcr) lower than 0.079 K/s. For both routes were determined the activation enthalpies for crystallization, that were 126 12 kJ/mol (for P2O5) and 110 32 kJ/mol (for H3PO4). The calculated Avrami n parameters, based on exothermic crystallization peaks, were 3.50 0.33 (for P2O5) and 3.09 0.91 (for H3PO4), considering data from the lowest heating rate (5 K/min). These values suggest that the DSC peaks should be associated to volume crystallization, due to La2O3 influence, and crystallization did not change significantly using different routes. |
Keywords: | Vidro Cristalização Crescimento de Cristais Não-Isotermico DSC Nucleação Cinetica |
URI: | http://www.repositorio.ufba.br/ri/handle/ufba/577 |
Issue Date: | 2006 |
Appears in Collections: | Artigo Publicado em Periódico (PEI) |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
AssesmentGFACrystallizationPhosphate-ML61-Nascimento.pdf | 269,06 kB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.